Waterproof transformer epoxy potting 9000A/113B

Features】
● This product is black epoxy potting room temperature, low viscosity, good fluidity, easy to penetrate into the gap in the product;
● can be room temperature or in temperature curing, curing rate is moderate;
● no bubbles after curing, the surface smooth, has good gloss, high hardness;
● cured a flame retardant, acid properties, and moisture properties of good water and oil dust, heat and humidity and atmospheric aging;
● cured with good insulation, compressive strength, high bonding strength of electrical and physical characteristics.

Potting

Insulating adhesive

Sealant
 

The scope of application
● For those who require infusion sealing, packaging protection, insulation or other proof of electronic products can be used;
● Widely used in water-proof transformer, AC capacitors, ignition coil, negative ion generator, aquarium water pumps, ignition coils, power modules, electronic controllers and other electronic components of the casting;
● does not apply to flexible or soft shell encapsulating products.
【Appearance】 transitivity
Model 9000A 113B
Color black viscous liquid brown liquid
The proportion of 25 ℃ 1.55g / cm 3 1.05g / cm 3
Viscosity 25 ℃ 5500-6000cps 70-90cps
Shelf life 25 ℃ 6 months 6 months
Usage
Distribution ratio: A: B = 100:25 (weight ratio)
Use time: 25 ℃ × 40 分钟 (100g mixed content)
Curing conditions: 25 degrees / 24 hours or 60 ℃ × 3 小时
● casting products to the need to maintain dry, clean;
● Please check the A agent when used to observe whether there is settlement, and agent A, stir;
● Press the ratio of the amount taken, and the weighing accuracy, please remember that the ratio is the ratio of weight rather than volume, A, B agent to be mixed, stir in order to avoid incomplete cure;
● Stir the filling plastic please, and try to use the time you are finished using the glue has been mixed;
● perfusion, glue products will gradually penetrate into the gap, if necessary a second plastic irrigation;
● curing process, please keep the environment clean, to prevent impurities or dust into the surface of uncured glue.
【Characteristics】 after curing
Dielectric rate 1KHZ 3.75
Dielectric loss 1KHZ 0.02
Compressive Strength kg/mm2 24
Bending strength kg/mm2 11
Tensile strength kg/mm2 16.5
Impact strength kg/mm2/cm2 8.5
K 1KHZ 3.8 ~ 4.2
SHORE D 80 hardness
Heat distortion temperature ℃ 80
Volume resistivity 25 ℃ Ohm-cm 1.35 × 1015
Surface resistance 25 ℃ Ohm 1.2 × 1014
Withstand voltage 25 ℃ Kv / mm 16 ~ 18
【Note】
● use, please be sure to weigh accurately and fully stirred to ensure uniformity of product quality.
● The product began after the curing mixture, its viscosity will gradually increase, and will release some of the heat;
● glue mixed with the more the faster the reaction, curing speed will be faster, and may be accompanied by a lot of heat release, please pay attention to controlling the amount of time with plastic, because the reaction to speed up its time use also shortened the glue mixture used up as much as possible in a short time;
● use of time: is the condition at 25 ℃, 100g mixed viscosity glue after doubling time, not operational time, the glue should never be used;
● a handful of people will have prolonged exposure to glue mild skin irritation, mild itching, wearing protective gloves is recommended, please stick to the skin, wipe with acetone or alcohol, and use detergent;
● in a large number before you use a small amount of trial skills to master the use of products in order to avoid errors.
Storage and packaging】 【
● This product must be in a ventilated, cool, dry place sealed, shelf life of six months, expires by the pilot qualified to continue to use;
● Package size for each group of 36kg, which contains the main agent 25kg / barrel, curing agent 10kg / barrel.