Major Features 主要优点
Long open time 操作时间长
High shear and peel strength 高的剪切与高剥离强度
Excellent low temperature properties 优异的低温性能
Room temperature cure 常温固化
Controlled flow 流动性容易控制
PROPERTIES OF UNCURED MATERIAL 固化前材料性能
|
Property性能
|
Test Method测试方法
|
800A
|
800B
|
|
Color/appearance
颜色
|
Visual
目视
|
Creamy white, viscous/liquid
膏状白色粘稠液体
|
Amber Liquid
琥珀色液体
|
|
SpecificGrav密度, g/cc
|
ASTM D-792
|
1.12
|
1.10
|
|
Viscosity粘度(cP), 25ºC
|
ASTM D-2393
|
60,000 - 100,000
|
8,000 - 12,000
|
TYPICAL CURED PROPERTIES 固化后属性
|
Property
性能
|
Test Method
测试方法
|
Test Value
测试值
|
|
Hardness, casting after 15 minutes, Shore D 邵氏硬度，浇铸15分钟后
|
D-2240
|
75
|
|
Ultimate Tensile Strength
极限抗张强度, psi
|
D-638
|
5200
|
|
Elongation 生长率, %
|
D-638
|
7
|
|
Modulus 模量(psi)
|
D-638
|
400, 000
|
|
T- Peel Test 剥离测试(pli)
|
D-1876
|
50-60
|
|
Lap shear strength 搭接剪切强度, psi at 25C
|
ASTM D-1002
|
|
|
Galvanized Steel 镀锌钢
|
|
2500
|
|
Fibre reinforced composite 纤维增强复合材料
|
|
1500
|
|
Mineral filled PET plastics 矿物填充PET塑料
|
|
800
|
|
Aluminum (primered) 铝
|
|
5000
|
|
Aluminum (acid etched) 铝（酸腐蚀）
|
|
4200
|
Effects of application temperature on lap shear strength(LSS ) by ASTM D-1002
温度对搭接剪切的影响
Load applied 10 minutes after specimens reach test temperature当样品达到测试温度后10分钟
|
|
Test Temperature
|
LSS Value, psi
|
|
Al/Al
|
-60ºC
|
4700
|
|
Al/Al
|
82 ºC
|
1500
|
|
Al/Al
|
121 ºC
|
500
|
|
Al/Al
|
30 days salt spray
|
4000
|
|
Al/Al
|
30 days @ 60ºC/100% RH
|
3500
|
Directions for use使用方法
|
Reaction Ratio (by weight) 反应重量比
|
|
100A/49B
|
|
Reaction Ratio (by volume) 反应体积比
|
|
100A/50B
|
|
Pot Life (100 grams) 25°C 使用时间（100克）
|
ASTM D-2471
|
30 minutes
|
|
Pot Life (20 grams) 25°C 使用时间（20克）
|
|
60 minutes
|
Curing time table固化进度表:
3-5 days at 77؛F. or elevated temperatures for accelerated cure. 在25摄氏度下3-5天。或者在升高的温度下
加速固化
Shelf Life 保质期
Provided this material is stored under the recommended storage condition in the original container, it will remain in useable condition for
from date of shipping.
若该产品按照上述要求存储，并且是保存在原装容器内，从发货之日起，在一年内可以使用。