PROPERTIES OF UNCURED MATERIAL 固化前材料性能
|
Property
性能
|
Test Method
测试方法
|
|
|
|
Color/appearance
颜色/外观
|
Visual
|
Yellow,
黄色
|
Blue,
蓝色
|
|
Specific gravity
密度, g/cc
|
ASTM D-792
|
1.23
|
1.1
|
|
Viscosity
粘度 (cP), 25ºC
|
ASTM D-2393
|
Soft thixotropy
柔性触变膏体
|
Soft thixotropy
柔性触变膏体
|
TYPICAL PROPERTIES OF CURED MATERIAL 固化后材料典型物理性能
|
Property
性能
|
Test Method
测试方法
|
Typical Value
典型值
|
|
Tensile Strength
抗拉强度, N/mm2
|
ASTM D-638
|
71( 23°C)
24 ( 60°C)
|
|
Elongation 延长率 (%)
|
ASTM D-638
|
3
|
|
Modulus
模量 N/mm2
|
|
4050 ( 23°C) 2400 (60°C)
|
|
Impact Strength 冲击强度, J/m2
|
K 1C
|
2
|
|
Glass Transition Temperature
玻璃化转变温度, Tg per DSC, °C
|
ASTM D-4065
|
78
|
|
Heat Distortion Temperature
热变形温度, °C
|
|
70-75
|
|
Coefficient of Thermal Expansion
热膨胀系数, (in/in/°C), -50°C to +50°C
|
ASTM E-831
|
58 X 10-6
|
|
Curing Shrinkage收缩率, %
|
|
0.2
|
|
Roller Peel Strength 滚筒剥离强度, N/mm
|
ISO 4578
|
6
|
|
Lap shear strength 层间剪切强度, N/mm2
|
ASTM D-1002
|
|
|
Stainless Steel (grit blasted) 不锈钢（磨砂处理）
|
|
25
|
|
FRP Prepreg FRP预浸渍
|
|
11
|
|
Aluminum ( acid etched)铝（酸腐蚀）
|
30
|
|
|
Aluminum ( Chromate surface treated)
铝（铬酸盐表面处理）
|
Tested at -60 °C
|
20
|
|
Tested at 23 °C
|
25
|
|
|
Tested at 70 °C
|
21
|
|
|
Tested at 80 °C
|
18
|
|
|
Tested at 90 °C
|
11
|
|
|
Tested at 100 °C
|
8
|
|
|
Double lap shear strength, Epoxy Laminate
双层剪切强度, 环氧层压板, N/mm2
|
Tested at -20 °C
|
15
|
|
Tested at 23 °C
|
17
|
|
|
Tested at 50 °C
|
17
|
|
|
Environmental Resistance 耐候性
|
Immersion 浸渍
|
Strength 强度
|
|
90 days in lubricate oil 润滑油中90天
|
|
Slight change
轻微改变
|
|
90 days in fuel 燃油中90天
|
|
No change无变化
|
|
90 days in water at ambient condition 水中90天
|
|
No change无变化
|
|
90 days in tropical humidity 湿热90天
|
|
Slight change
轻微改变
|
DIRECTIONS FOR USE 使用指南
|
Mix Ratio (by weight) 树脂与固化剂重量比
|
100R/33H
|
|
Mix Ratio (by volume) 树脂与固化剂体积比
|
100R/40H
|
|
Pot Life (100 grams) 保质期（100g）, 25°C
|
4 hours
|
|
5cm radius bead 5cm 半径的球状, 25°C
|
2 hours
|
Curing time table 固化进度表：
Curing at 70℃ ×4 hours is recommended. 推荐固化温度70 ℃下固化4个小时。
|
Curing temperature固化温度
|
Curing time
固化时间（到1N/mm2）
|
Curing time
固化时间（到10N/mm2）
|
|
23 ℃
|
15 h
|
75 h
|
|
60 ℃
|
1.5 h
|
3 h
|